A company specializing in the production, research and development, and sales of steel wire ropes. It develops and produces supporting services for elevator rope manufacturers, focusing on 6 * 19 steel wire ropes. At the
- Product details
-
6×K36WS-FC 是一款 6 股 K 型压实瓦林吞 - 西鲁式股 + 纤维芯 的重型柔韧性钢丝绳，兼具高承载潜力、优异弯曲灵活性与轻量化特性，符合 GB/T 8918-2016《重要用途钢丝绳》标准，适用于中型履带吊副钩、港口件杂货起重机、建筑大型塔吊变幅机构、风电塔筒整体吊装辅助绳等对重载、频繁大角度弯曲、便捷运维有需求的作业工况。
型号含义拆解
型号部分 含义说明 6 外层为 6 个工作股，对称排列设计配合交叉捻向结构，相比 8 股型号单股截面更大，承载效率高，同时可有效抵消重载时的扭转扭矩，实现低旋转特性，避免重型吊装时吊钩打转、货物摆动 ×K36WS K 型压实瓦林吞 - 西鲁式股（WS=Warrington-Seale 复合结构），每股由 36 根粗细交替钢丝排布而成，经冷压实工艺处理后股径缩小、钢丝呈面接触状态，金属截面积利用率大幅提升，抗疲劳、抗磨损性能远超普通捻制股 -FC 绳芯为 纤维芯（Fiber Core），材质多为聚丙烯或剑麻，相比独立钢绳芯（IWRC）重量更轻、柔韧性更好，适配中型卷筒的频繁大角度弯曲作业，降低设备传动系统负载损耗 一、基础结构参数
参数项 详细说明 结构组成 6 个 K 型压实瓦西式外层股 + 纤维芯（FC，聚丙烯 / 剑麻材质）；外层股与绳芯采用交叉捻向（外层右捻、芯左捻），绳体圆整度高，旋转扭矩低，柔韧性优于同规格 6×K36WS-IWRC 型号 钢丝材质 优质高碳钢（#82B、#925），经冷拔强化 + 股压实处理；外层股钢丝表面可选热镀锌 / 电镀锌 / 光面，按需匹配防腐与耐磨需求 表面处理 1. 热镀锌：镀层厚 30~60μm，适用于沿海高盐雾、矿山潮湿等中强腐蚀重载场景2. 电镀锌：镀层厚 8~15μm，适用于干燥室内重型起重工况3. 光面：无镀层，需定期加注专用润滑脂，适用于无尘高精度重型吊装场景 直径范围 常见 18~65mm，主流应用 28~55mm 重型提升 / 牵引场景 公称抗拉强度 高碳钢型：1770MPa、1960MPa、2160MPa（重型吊装设备优先选用 1960MPa 等级，兼顾强度与柔韧度） 重量系数 0.420~0.450（比同规格 6×K36WS-IWRC 轻 24%~28%，轻量化优势显著） 最小破断拉力系数 0.320~0.340（K 型压实工艺提升金属利用率，比普通 6×36WS+FC 系列提升 16%~21%，满足重载作业强度需求） 二、典型力学性能表（1960MPa 热镀锌 + 聚丙烯纤维芯）
公称直径（mm） 参考重量（kg/100m） 最小破断拉力（kN） 适用场景 28 420 1950 中型履带吊副钩绳、港口门式起重机辅助起升绳 38 780 3700 建筑大型塔吊变幅绳、风电塔筒整体吊装辅助绳 48 1250 5900 港口件杂货起重机主绳、矿用提升设备辅助绳 58 1850 8600 中型港口卸船机主绳、重型预制件转运绳 注：若选用剑麻纤维芯，耐温性（≤120℃）优于聚丙烯芯，但耐水性较差，重量略增 3%~5%；热镀锌处理对破断拉力的影响小于 2%。三、核心特性
- 重载高柔韧性，适配频繁大角度弯曲6 股大截面结构保障重载承载能力，纤维芯的弹性缓冲作用让绳体弯曲半径比同规格钢芯型号小 26%~31%，能适配中型卷筒的高频次起升下放、大角度换向作业，尤其适合塔吊变幅、履带吊副钩等需要频繁调整吊装角度的重型场景。
- 轻量化设计，降低重型设备负载损耗纤维芯替代钢绳芯，整体重量大幅降低，减少重型起重设备的整机负载与能耗，同时降低人工搬运、安装的难度，延长设备传动系统与卷筒的使用寿命，适配需要频繁转场的中型吊装设备。
- 耐磨耐疲劳，使用寿命长瓦林吞 - 西鲁式股的外层粗钢丝与滑轮、卷筒接触面积均匀，磨损速率低；压实工艺让股内 36 根钢丝紧密贴合，减少微动摩擦损耗，耐疲劳性能是普通 6×36WS+FC 钢丝绳的 1.8~2.2 倍，降低重型设备运维成本。
- 防腐性能可控，适配多环境重型作业热镀锌镀层附着力强，可抵御沿海盐雾、矿山潮湿等腐蚀环境；搭配纤维芯专用防腐润滑脂，既能润滑钢丝接触面，又能防止纤维芯受潮腐烂，维护周期可延长至普通纤维芯钢丝绳的 1.5 倍。
四、选型与使用要点
- 安全系数选择
- 中型履带吊副钩 / 建筑大型塔吊变幅：7~9 倍
- 港口件杂货起重机 / 风电塔筒辅助吊装：9~11 倍
- 严禁用于矿山竖井提升、超重型设备长期悬挂、高温（＞120℃）等重载高危工况
- 纤维芯选型建议
- 户外潮湿 / 沿海腐蚀环境 → 聚丙烯纤维芯（耐水耐腐蚀，性价比高）
- 钢厂附近等高温作业场景 → 剑麻纤维芯（耐温性好，需做好防水防护）
- 高精度无尘吊装场景 → 改性聚丙烯纤维芯（低粉尘脱落，清洁度高）
- 卷筒与滑轮匹配
- 卷筒直径 ≥ 钢丝绳直径的 20~25 倍
- 滑轮直径 ≥ 钢丝绳直径的 18~22 倍
- 滑轮槽底需为圆弧浅槽精密加工，与绳径精准匹配，避免股丝受力不均引发断丝
- 维护注意事项
- 定期加注 纤维芯钢丝绳专用防腐润滑脂，采用低压注脂方式，确保润滑脂渗透至股间缝隙，不可使用钢绳芯专用润滑脂（易堵塞纤维芯孔隙）
- 检查重点为 股端断丝、绳径磨损、纤维芯外露、镀层脱落，出现单股 2 丝断丝或纤维芯外露时需立即报废
- 运输与存放时需使用专用大型支架盘卷，避免挤压变形、尖锐物划伤镀层；长期存放置于干燥通风环境，每 3 个月翻动一次，防止局部锈蚀
需要我帮你整理6×K36WS-FC 与 6×K36WS-IWRC 的性能对比表吗？6×K36WS-EPIWRC6×K36WS-EPIWRC 钢丝绳核心参数与性能
6×K36WS-EPIWRC 是一款 6 股 K 型压实瓦林吞 - 西鲁式股 + 聚合物填充独立钢丝绳芯 的高强度重型低旋转压实钢丝绳，符合 GB/T 8918-2016《重要用途钢丝绳》标准，适用于大型履带吊主钩、港口集装箱起重机、海上平台吊装设备、矿用提升绞车等对超高承载、抗挤压、多层缠绕、低维护有严苛要求的重型作业工况。型号含义拆解
型号部分 含义说明 6 外层为 6 个工作股，对称排列设计配合交叉捻向结构，相比 8 股型号刚性更强、单股载荷分布更均匀，可有效抵消重载吊装时的扭转扭矩，实现低旋转特性，避免重型货物摆动、吊钩打转引发安全隐患 ×K36WS K 型压实瓦林吞 - 西鲁式股（WS=Warrington-Seale 复合结构），每股由 36 根粗细交替钢丝排布而成，经冷压实工艺处理后股径缩小、钢丝呈面接触状态，金属截面积利用率大幅提升，抗疲劳、抗磨损性能远超普通捻制股 -EPIWRC 聚合物填充独立钢丝绳芯（Epoxy/Polymer Impregnated IWRC），在独立钢丝绳芯（常规 7×37 重型结构）的股间与芯外填充高分子聚合物材料，既保留 IWRC 的高径向支撑力与抗挤压性能，又提升防腐、减摩、抗冲击特性，显著延长维护周期 一、基础结构参数
参数项 详细说明 结构组成 6 个 K 型压实瓦西式外层股 + 聚合物填充独立钢丝绳芯；外层股与绳芯采用交叉捻向（外层右捻、芯左捻），绳体圆整致密，旋转扭矩极低，抗挤压性能优于普通 IWRC 型号，柔韧性优于同规格无填充钢芯型号 钢丝材质 优质高碳钢（#82B、#925），经冷拔强化 + 股压实处理；外层股与绳芯钢丝表面可选热镀锌 / 电镀锌 / 光面，按需匹配不同腐蚀工况 表面处理 1. 热镀锌：镀层厚 30~60μm，适用于沿海高盐雾、矿山潮湿等强腐蚀重载场景2. 电镀锌：镀层厚 8~15μm，适用于干燥室内重型起重工况3. 光面：无镀层，需定期加注专用润滑脂，适用于无尘高精度重型吊装场景 直径范围 常见 22~75mm，主流应用 32~65mm 重型提升 / 牵引场景 公称抗拉强度 高碳钢型：1770MPa、1960MPa、2160MPa（重型重载设备优先选用 1960MPa 等级，兼顾强度与耐疲劳性） 重量系数 0.580~0.610（比同规格 6×K36WS-IWRC 重 3%~5%，比 6×K36WS-FC 重 30%~35%，平衡强度与缓冲性能） 最小破断拉力系数 0.420~0.440（K 型压实工艺 + EPIWRC 绳芯协同作用，金属利用率比普通 6×36WS+FC 系列提升 22%~27%） 二、典型力学性能表（1960MPa 热镀锌 + EPIWRC 芯）
公称直径（mm） 参考重量（kg/100m） 最小破断拉力（kN） 适用场景 32 750 3500 中型履带吊主钩绳、港口门式起重机主起升绳 42 1320 6200 大型履带吊主钩绳、矿用提升绞车主绳 52 2050 9600 港口集装箱起重机主绳、海上平台吊装设备主绳 62 2920 13800 超重型建筑构件吊装绳、大型浮吊主绳 注：热镀锌处理对破断拉力的影响小于 2%；聚合物填充层可降低股间磨损，相比普通 IWRC 型号维护周期延长 70%~90%，大幅降低重型设备运维成本。三、核心特性
- 超高承载抗挤压，适配重型多层缠绕6 股大截面结构 + K 型压实工艺，结合 EPIWRC 芯的高支撑刚度，让钢丝绳可承受大型卷筒数十层缠绕的挤压应力，股间变形量比普通 IWRC 型号减少 35%~40%，适配矿用提升、港口集装箱吊装等高频次重载作业。
- 低旋转高稳定，保障重型精准吊装6 股对称排列 + 交叉捻向设计，配合聚合物填充层的应力缓冲作用，重载吊装时吊钩旋转幅度控制在极小范围，避免超重型货物摆动引发的安全事故，满足海上平台构件、万吨级预制件的高精度吊装需求。
- 防腐缓冲双优，延长使用寿命热镀锌镀层 + 聚合物填充层形成双重防腐屏障，隔绝潮气与腐蚀介质，适配沿海、矿山等恶劣环境；填充层同时缓冲冲击载荷，减少钢丝间的微动摩擦，耐疲劳性能是普通 6×36WS+FC 钢丝绳的 2.2~2.6 倍。
- 低维护成本，提升作业效率聚合物填充层自带减摩效果，无需频繁加注润滑脂，相比普通钢芯钢丝绳的维护频次降低 60% 以上，减少设备停机时间，提升重型吊装作业的整体效率。
四、选型与使用要点
- 安全系数选择
- 中型履带吊主钩 / 港口门式起重机：5~7 倍
- 大型履带吊主钩 / 矿用提升绞车：6~8 倍
- 海上平台吊装 / 超重型构件吊装：7~9 倍
- 严禁用于强酸碱腐蚀无防护、超高温（＞200℃）等极端工况
- 环境适配原则
- 干燥室内重型起重 → 电镀锌全绳型号
- 户外 / 矿山 / 沿海强腐蚀环境 → 热镀锌型号，定期抽检填充层完整性
- 强腐蚀环境 → 搭配聚氨酯（PU）护套，隔绝腐蚀介质
- 卷筒与滑轮匹配
- 卷筒直径 ≥ 钢丝绳直径的 29~34 倍
- 滑轮直径 ≥ 钢丝绳直径的 26~31 倍
- 滑轮槽底需为圆弧深槽精密加工，与绳径精准匹配，避免股丝受力不均引发断丝
- 维护注意事项
- 定期加注 钢绳芯专用防腐润滑脂，采用高压注脂设备，确保润滑脂渗透至股间缝隙；严禁拆解绳芯，避免破坏聚合物填充层
- 检查重点为 股端断丝、绳径磨损、镀层脱落、填充层鼓包或开裂，出现单股 3 丝断丝或填充层大面积破损时需立即报废
- 运输与存放时需使用专用大型支架盘卷，避免挤压变形、尖锐物划伤镀层；长期存放置于干燥通风环境，定期检查防锈情况
related products
Product Inquiry
Please leave your message, we will contact you quickly after receiving it, thank you for your support!
common problem
Q
What kind of lubricant can prevent wire rope damage?
A
First, the smooth oil has good fluidity and soaking ability, allowing it to quickly enter the inside of the rope and the rope core when the wire rope is smooth pretreated, and can play a role in preventing bacteria from multiplying inside the rope core fibers.
Second, the lubricating oil adhered to the wire rope will not be easily wiped off, and the smoothing effect will not be affected within the specified temperature range. In addition, the lubricating oil with adhesive function can also prevent skid, which provides assistance for the friction of the elevator wire rope.
Third, it has a high oil film strength, which can resist the extremely high pressure between the steel wires in contact with each other under extremely heavy load, and can also resist decomposition and transformation.
Fourth, smooth oil has high cohesion, which can avoid the dripping of smooth oil, centrifugal loss when there is no exercise, and avoid grease waste and pollution to other equipment.
Fifth, it does not contain ingredients that can cause corrosion and rust in the steel wire rope, and the effect of anti-corrosion and anti-rust is better.
Sixth, its self-correcting ability is strong. When the wire rope is used, it constantly twists and turns, which will cause the surface oil film to continuously knead and expand. This requires a soft and high-temperature oil film to maintain the rope body from cracking.
Second, the lubricating oil adhered to the wire rope will not be easily wiped off, and the smoothing effect will not be affected within the specified temperature range. In addition, the lubricating oil with adhesive function can also prevent skid, which provides assistance for the friction of the elevator wire rope.
Third, it has a high oil film strength, which can resist the extremely high pressure between the steel wires in contact with each other under extremely heavy load, and can also resist decomposition and transformation.
Fourth, smooth oil has high cohesion, which can avoid the dripping of smooth oil, centrifugal loss when there is no exercise, and avoid grease waste and pollution to other equipment.
Fifth, it does not contain ingredients that can cause corrosion and rust in the steel wire rope, and the effect of anti-corrosion and anti-rust is better.
Sixth, its self-correcting ability is strong. When the wire rope is used, it constantly twists and turns, which will cause the surface oil film to continuously knead and expand. This requires a soft and high-temperature oil film to maintain the rope body from cracking.
Q
What are the classifications of wire ropes?
A
1, electric hoist wire rope: 6 * 37 + FC- 11/13/15/17.5
2, tower crane wire rope and multi-strand non-rotating wire rope: 6 * 19 + FC- 12/12.5, 6 * 37-13/14, 6 * 29FI + FC- 12/12.5, 4v39s + 5FC- 12/13/14, 35W * 7-12/13/14
3, car crane does not rotate wire rope: 4V39S + 5FC- 10/12/13/14/16/17, 35W * 7-10/12/13/14/15/16/17/18/20/22
4, pile driver flat wire rope: K6K36WS + IWR-/17.5/24/26/28/30/32/34/36/40/42/46
5, rotary excavator flat wire rope: 35W * K7- 24/26/28/30/32/36/40
6, dock crane wire rope: 6 * 36WS + IWR- 17.5/19 5/21.5/24/26
7, mine wire rope 6 * 19 + FC- 12.5/14/15.5/17/18.5/21 5/24.5/26/28, 6 * 19S + FC- 12.5/14/15.5/17/18.5/21 5/24.5
8, elevator wire rope: 8 * 19S + FC- 10/11/12/13/16
9. Hot-dip galvanized hanging basket wire rope: 4 * 31WS + PPC- 8.3/8
10. Hot-dip galvanized wire rope: 6 * 19/6 * 37/6 * 36WS/8 * 61/8 * 36WS/
11, galvanized wire rope: 6 * 7 + FC-/2/3/4
6 * 19 + FC-5/6/7 7/9.3/11, 6 * 12 + 7FC-5/6/7. 7/9.3/11, 7 * 19-5/6/8/10, 19 * 7-4/5/6/8/10, 6 * 37 + FC-8.7/9 3/11/13/15/17.5/19.5
12. Large diameter wire rope: above 60MM
13. Wire rope rigging (insertion, pressing, pouring, connectors, etc.):
14, coated wire rope: 2-3/3 - 4/4-5/5-6/6 - 8/8-12/12-15
15, binding wire rope: 6 * 12/6 * 15-13/14/15
The front represents the structure, and the back represents the diameter. For example: 6 * 37 + FC-11, the representative structure is 6 * 37 + FC, diameter: 11MM
2, tower crane wire rope and multi-strand non-rotating wire rope: 6 * 19 + FC- 12/12.5, 6 * 37-13/14, 6 * 29FI + FC- 12/12.5, 4v39s + 5FC- 12/13/14, 35W * 7-12/13/14
3, car crane does not rotate wire rope: 4V39S + 5FC- 10/12/13/14/16/17, 35W * 7-10/12/13/14/15/16/17/18/20/22
4, pile driver flat wire rope: K6K36WS + IWR-/17.5/24/26/28/30/32/34/36/40/42/46
5, rotary excavator flat wire rope: 35W * K7- 24/26/28/30/32/36/40
6, dock crane wire rope: 6 * 36WS + IWR- 17.5/19 5/21.5/24/26
7, mine wire rope 6 * 19 + FC- 12.5/14/15.5/17/18.5/21 5/24.5/26/28, 6 * 19S + FC- 12.5/14/15.5/17/18.5/21 5/24.5
8, elevator wire rope: 8 * 19S + FC- 10/11/12/13/16
9. Hot-dip galvanized hanging basket wire rope: 4 * 31WS + PPC- 8.3/8
10. Hot-dip galvanized wire rope: 6 * 19/6 * 37/6 * 36WS/8 * 61/8 * 36WS/
11, galvanized wire rope: 6 * 7 + FC-/2/3/4
6 * 19 + FC-5/6/7 7/9.3/11, 6 * 12 + 7FC-5/6/7. 7/9.3/11, 7 * 19-5/6/8/10, 19 * 7-4/5/6/8/10, 6 * 37 + FC-8.7/9 3/11/13/15/17.5/19.5
12. Large diameter wire rope: above 60MM
13. Wire rope rigging (insertion, pressing, pouring, connectors, etc.):
14, coated wire rope: 2-3/3 - 4/4-5/5-6/6 - 8/8-12/12-15
15, binding wire rope: 6 * 12/6 * 15-13/14/15
The front represents the structure, and the back represents the diameter. For example: 6 * 37 + FC-11, the representative structure is 6 * 37 + FC, diameter: 11MM
Copyright © 2012-202X Jiangsu Dingtian Technology New Materials Co., Ltd. All rights reserved